SAE1141H钢花键轴热处理后开裂原因分析

腊月:快赢彩票网    发布时间:2017-12-13 点击量:
SAE1141H钢花键轴热处理后开裂原因分析Crack reason analysis on SAE1141H steel spline shaft after heat treatment用显微组织观察和超声波探伤等方法,分析研究了SAE1141H钢花键轴经中频感应加热淬火后检验时在线切割取样过程中出现的开裂现象。结果表明,花键轴内部并没有裂纹,这种开裂是中频感应加热淬火后花键轴中的残余应力在切割过程中释放的结果,它起源于硫化物的偏聚区并沿着硫化物扩展。通过改变检验时取样的切割路线可以有效避免这种开裂现象。 Cracks on SAE1141H free-cuRing steel spline shaft.occurred during linear cutting samples for check after medium—frequency induction hardening,were analyzed with observation of microstructure and supersonic inspection etc.The results show that there are actually no crocks inside of the shaft and the cracks are caused by the release of residual stress during sampling after medium·frequency induction hardening.The cracks originate from the accumulation zone of sulphides and propagate along with the sulphides.It Can be effectively avoided by changing the cutting route during sampling. 全文下载:

    作为值得信赖的合作伙伴和高品质金属合金的半成品供应商,艾荔艾拥有完善的服务体系和专业的团队。在同客户交易的过程中,我们力求根据不同的应用需求将我们的产品做到精益求精。针对当前和未来的市场需求,艾荔艾致力于为客户提供最佳的金属材料解决方案。

    AILIAI has been a reliable partner and supplier of sophisticated and high-quality semi-finished products maed of alloys. In dialogue with our customers, we optimise our products to meet the specific application requirements. AILIAI develops the best alloy material solutions for current and future challenges.

    获取更多我们供应的合金和服务信息,请致电086-021-67660801或发电子邮件kefu@ailiaigroup.com联系我们,您也可以通过,脸书我们互动。

    For more information on the alloys and services that we supply,  at 086-021-67660801 or email us at kefu@ailiaigroup.com. You can also get in touch on social media, we are constantly active on , , Facebook and .